Abstract: An open-pored metal body, which is formed having a core layer (A) consisting of Ni, Co, Fe, Cu, Ag or an alloy formed having one of said chemical elements, wherein one of said chemical elements is present in the alloy at more than 25 at %, and a gradated layer (B) is formed on surfaces of the core layer (A), said gradated layer being formed by intermetallic phase or mixed crystals of Al, and a layer (C), which is formed having aluminum oxide, is formed on the gradated layer (B).

Abstract: A method of manufacturing a catalyst material includes the steps of: providing a body having an open-porous foam structure and comprising at least a first metal or alloy; providing particles, each of which particles comprising at least a second metal or alloy; distributing the particles on the body; forming a structural connection between each of at least a subset of the particles and the body; and forming an oxide film on at least the subset of the particles and the body, wherein the oxide film has a catalytically active surface.

Abstract: An open-pored metal body, which is formed having a core layer (A) consisting of Ni, Co, Fe, Cu, Ag or an alloy formed having one of said chemical elements, wherein one of said chemical elements is present in the alloy at more than 25 at %, and a gradated layer (B) is formed on surfaces of the core layer (A), said gradated layer being formed by intermetallic phase or mixed crystals of Al, and a layer (C), which is formed having aluminum oxide, is formed on the gradated layer (B).

Abstract: The invention relates to a method for producing open-pore molded metal bodies which have a modified surface. The surface of an open-pore molded metal body said molded body being used as a semi-finished product, is coated with particles of a chemical compound of a metal on particles of the metal which can be reduced or thermally or chemically decomposed in a thermal treatment. After the coating process, at least one thermal treatment is carried out, in which the produced metal particles are connected to the surface of the semi-finished product and/or adjacent produced particles via sintered necks or sintered bridges such that the specific surface area of the obtained open-pore molded body is increased to at least 30 m2/l and/or at least by a factor of 5 in comparison to the starting material of the uncoated metal semi-finished product.

Abstract: A method for producing open-pored molded bodies made of a metal. The surface of the metal open-pored molded body being used as a semi-finished product, is coated with particles of the same metal with which the semi-finished product is made or with particles of a chemical compound of the metal the semi-finished product is made, wherein the compound or particles can be reduced or thermally or chemically decomposed in a thermal treatment. After the coating process, a thermal treatment in a suitable atmosphere is carried out, in which the particles are connected to the surface of the semi-finished product and/or adjacent particles such that the specific surface area of the obtained open-pore molded body is increased to at least 30 m2/l and/or at least by a factor of 5 in comparison to the starting material.

Abstract: A metallic foam body containing an alloy skin which is up to 50 ?m thick can be obtained by a process including (a) providing a metallic foam body comprising a first metallic material; (b) applying a second metallic material which contains a first metallic compound that is leachable as such and/or that can be transformed by alloying into a second metallic compound that is leachable and different from the first metallic compound on a surface of the foam body (a), by coating the metallic foam body with an organic binder and a powder of the second metallic material; (c) forming a skin on foam body (b) by alloying the first and the second metallic material; and (d) leaching out with a leaching agent at least a part of the first and/or the second metallic compound.

Abstract: Disclosed are an open-porous metal foam and a method for manufacturing the same. An open-porous metal foam according to an exemplary embodiment of the present invention is made of an iron-based alloy including 15 wt % or more of chrome and 5 wt % or more of aluminum. The open-porous metal foam is a semi-product that is formed of iron or the iron-based alloy that does not include chrome and aluminum or includes a smaller amount of chrome and aluminum in the powder when manufacturing, and the surface and the open pore thereof are uniformly coated with the powder of the iron-chrome-aluminum alloy and the organic binding agent. When heat treatment is performed under a reduction atmosphere, sintering is performed.

Abstract: Disclosed are an open-porous metal foam and a method for manufacturing the same. An open-porous metal foam according to an exemplary embodiment of the present invention is made of an iron-based alloy including 15 wt % or more of chrome and 5 wt % or more of aluminum. The open-porous metal foam is a semi-product that is formed of iron or the iron-based alloy that does not include chrome and aluminum or includes a smaller amount of chrome and aluminum in the powder when manufacturing, and the surface and the open pore thereof are uniformly coated with the powder of the iron-chrome-aluminum alloy and the organic binding agent. When heat treatment is performed under a reduction atmosphere, sintering is performed.

Abstract: Disclosed are an open-porous metal foam and a method for manufacturing the same. An open-porous metal foam according to an exemplary embodiment of the present invention is made of an iron-based alloy including 15 wt % or more of chrome and 5 wt % or more of aluminum. The open-porous metal foam is a semi-product that is formed of iron or the iron-based alloy that does not include chrome and aluminum or includes a smaller amount of chrome and aluminum in the powder when manufacturing, and the surface and the open pore thereof are uniformly coated with the powder of the iron-chrome-aluminum alloy and the organic binding agent. When heat treatment is performed under a reduction atmosphere, sintering is performed.